Demonstration kit and method for enhancing and/or demonstrating photoactive properties

ABSTRACT

A method is provided for simulating and/or demonstrating and/or enhancing photoactive properties, such as hydrophilicity, of a surface, such as a photoactive surface. One embodiment includes providing a photoactive surface and applying a peroxide-containing material, such as an aqueous hydrogen peroxide solution, over at least a portion of the surface. An optional resinous layer, such as an at least partly hydrolyzed polymethoxysiloxane layer, can be applied over the surface. A kit to practice the method and an article made using the method are also provided.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. application Ser. No. 10/657,350filed Sept. 8, 2003, which claims the benefits of U.S. ProvisionalApplication Ser. No. 60/411,796 filed Sept. 18, 2002, all of whichapplications are herein incorporated by reference in their entirety.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates generally to the demonstration of photoactiveproperties, such as hydrophilicity, on a surface and, more particularly,to a method and kit to demonstrate and/or simulate one or morephotoactive properties of a surface in the absence of or at low levelsof activating radiation.

2. Technical Considerations

Photoactive substrates have found widespread acceptance in many fields.These photoactive substrates can be photocatalytic and/or hydrophilic(such as photohydrophilic). By “photoactive” or “photoactively” is meantthe capability to generate one or more physical or chemical effects uponexposure to certain wavelengths of electromagnetic energy. These effectscan be caused, for example, by the photogeneration of an electron-holepair when illuminated by activating radiation of a particular frequency.The activating radiation is typically in the ultraviolet (UV) or visibleranges of the electromagnetic spectrum. By “UV range” is meantelectromagnetic radiation in the range of 280 nanometers (nm) up to 395nm. By “visible range” is meant electromagnetic radiation in the rangeof 395 nm to 800 nm. By “photocatalytic” is meant a surface, such as acoating, having self-cleaning properties. By “self-cleaning” is meant asurface which upon exposure to electromagnetic radiation in thephotoabsorption band of the surface material (i.e., activatingradiation) interacts with organic contaminants on the surface to degradeor decompose at least some of the organic contaminants. By “hydrophilic”or “hydrophilicity” is meant water wetting. By “photohydrophilic” or“photohydrophilicity” is meant a surface upon which the contact angle ofa water droplet decreases with time as a result of exposure of thesurface to electromagnetic radiation within the photoabsorption band ofthe surface (e.g., coating). By “photoabsorption band” is meant therange of electromagnetic radiation absorbed by a material to render thematerial photoactive. For photohydrophilicity for example, the contactangle of a water droplet on the surface can decrease to a value lessthan 15°, such as less than 10°, and can become superhydrophilic, e.g.,decrease to less than 5°, after exposure to activating radiation in thephotoabsorption band of the material for a time period and at anintensity sufficient to activate the material.

While photoactive articles, such as architectural windows having aphotoactive surface or coating, provide advantages over non-photoactivearticles, problems can arise in demonstrating such photoactiveproperties and/or articles to a potential customer. For example, many ofthe commercially available photoactive windows are “UV photoactive”,meaning that the windows exhibit photoactivity only upon exposure toelectromagnetic radiation in the UV range. Since only about 3% to 5% ofthe solar energy that reaches the earth's surface is in this wavelengthrange, the photoactive window to be demonstrated may have to be exposedto solar energy for a sufficient period of time to activate the windowbefore the photoactive properties of the window can be demonstrated to acustomer. Other windows are “visibly photoactive”, meaning that theirphotoabsorption band is at least partly in the visible range. By“activate” is meant to expose the photoactive surface to electromagneticradiation within the photoabsorption band of the photoactive materialfor a period of time sufficient for the photoactive material to begin todisplay photoactive properties, such as but not limited tophotohydrophilicity and/or photocatalytic activity. This can mean havingto maintain a demonstration window outdoors at a particular location andrequire potential customers to come to that location during daylighthours (when the window is active due to the presence of solar radiation)to demonstrate the benefits of the photoactive surface to the customer.Should it be desired to demonstrate the photoactive window to a customerduring the nighttime or indoors, a light source, such as a conventionalmercury or black lamp, may be required to provide sufficient energy torender the window photoactive. Such problems are compounded if it isdesired to have a salesman visit various customers' locations with ademonstration substrate (such as a sample of a photoactive window or aphotoactive substrate) to demonstrate the photoactive properties of thesubstrate to customers. The salesman may keep the demonstrationsubstrate in his car (such as in the trunk or other areas where thesubstrate is not accessible to solar energy) and, hence, degrade thephotoactivity level of the substrate surface to the point where thephotoactive material no longer displays one or more photoactiveproperties, such as hydrophilicity and/or photocatalysis. Thisdegradation can be caused, for example, by a build-up of contaminants onthe surface. Moreover, it would be difficult to demonstrate thephotoactive window at night or indoors without requiring the salesman tocarry a portable light source to activate the substrate tophotocatalytically degrade contaminants on the surface.

Therefore, it would be advantageous to provide a method of demonstratingor simulating at least some of the photoactive properties of aphotoactive surface in the absence of or at low levels of activatingradiation. It would also be advantageous to simulate at least somephotoactive properties, such as hydrophilicity, on a non-photoactivesurface.

SUMMARY OF THE INVENTION

A method is provided for simulating and/or demonstrating and/orenhancing at least one photoactive property (such as hydrophilicity) ofa photoactive surface. The method includes providing a surface, such asa photoactive surface, and applying at least one peroxide-containingmaterial over at least a portion of the surface. In one embodiment, thesurface comprises titania and the peroxide material comprises hydrogenperoxide. In one embodiment, the peroxide coated surface can be exposedto electromagnetic energy having one or more wavelengths in the visibleregion. Additionally or alternatively, at least one at least partiallyhydrolyzed polyalkoxysiloxane can be deposited over at least a portionof the surface that has been activated or treated with a materialcontaining hydrogen peroxide.

A method is provided for demonstrating and/or simulating and/orenhancing the hydrophilicity of a surface. The method comprisesproviding a substrate having a photoactive surface, applying an at leastpartially hydrolyzed polyalkoxysiloxane material over at least a portionof the surface, and optionally applying at least one peroxide-containingmaterial over at least a portion of the surface.

A method is provided for demonstrating the hydrophilicity of aphotoactive surface or coating by exposing the surface toelectromagnetic radiation having one or more wavelengths in the visibleregion. The method includes providing a surface, such as a photoactivesurface comprising titania, and applying a peroxide material, such as anaqueous solution comprising 1 wt. % to 30 wt. % hydrogen peroxide, overat least a portion of the photoactive surface.

A method is provided for demonstrating and/or simulating one or morephotoactive properties, such as hydrophilicity, on a non-photoactivesurface. The method includes providing a non-photoactive surface, suchas glass, and applying at least one peroxide-containing material and/orat least one at least partially hydrolyzed polyalkoxysiloxane materialover at least a portion of the surface.

A kit is provided for demonstrating and/or simulating the hydrophilicityof a photoactive coating in the absence of or at low levels ofactivating radiation. The kit includes a container comprising an aqueousperoxide material, such as hydrogen peroxide, and optionally at leastone applicator. The kit can also optionally include one or more of acontainer of an at least partially hydrolyzed polyalkoxysiloxanematerial (such as at least partially hydrolyzed polymethoxysiloxane), acontainer of water, one or more applicator pads, a substrate having asurface with at least a portion of the surface comprising a photoactivematerial, and a stand to hold the substrate. The kit can also be used tosimulate photoactive hydrophilicity on a non-photoactive surface.

An article of the invention comprises a surface, such as a UVphotoactive surface and/or visible photoactive, and at least oneperoxide-containing material and/or at least one at least partiallyhydrolyzed polyalkoxysiloxane material deposited over the surface. Inone embodiment, the surface comprises titania. In one embodiment, theperoxide-containing material comprises hydrogen peroxide. Thepolyalkoxysiloxane material can comprise at least partially hydrolyzedpolymethoxysiloxane.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a side, sectional view (not to scale) of a portion of aphotoactive substrate demonstrating features of the invention;

FIG. 2 is a front view of a demonstration kit (not to scale)incorporating features of the invention; and

FIG. 3 is a graph of absorbance versus UV exposure time for severalsample substrates incorporating features of the invention.

DESCRIPTION OF THE INVENTION

As used herein, spatial or directional terms, such as “inner”, “outer”,“above”, “below”, “top”, “bottom”, and the like, relate to the inventionas it is shown in the drawing figures. However, it is to be understoodthat the invention may assume various alternative orientations and,accordingly, such terms are not to be considered as limiting. Further,all numbers expressing dimensions, physical characteristics, processingparameters, quantities of ingredients, reaction conditions, and the likeused in the specification and claims are to be understood as beingmodified in all instances by the term “about”. Accordingly, unlessindicated to the contrary, the numerical values set forth in thefollowing specification and claims are approximations that may varydepending upon the desired properties sought to be obtained by thepresent invention. At the very least, and not as an attempt to limit theapplication of the doctrine of equivalents to the scope of the claims,each numerical value should at least be construed in light of the numberof reported significant digits and by applying ordinary roundingtechniques. Moreover, all ranges disclosed herein are to be understoodto encompass any and all subranges subsumed therein. For example, astated range of “1 to 10” should be considered to include any and allsubranges between (and inclusive of) the minimum value of 1 and themaximum value of 10; that is, all subranges beginning with a minimumvalue of 1 or more and ending with a maximum value of 10 or less, e.g.,5.5 to 10. Further, as used herein, the terms “deposited over” or“provided over” mean deposited or provided on but not necessarily incontact with the surface. For example, a coating “deposited over” asubstrate does not preclude the presence of one or more other coatingfilms of the same or different composition located between the depositedcoating and the substrate. Additionally, all percentages disclosedherein are “by weight” unless indicated to the contrary. All referencesreferred to herein (such as but not limited to issued patents and patentapplications) are to be understood to be incorporated in their entirety.The terms “polymer” or “polymeric” include oligomers, homopolymers,copolymers, and terpolymers.

To describe the general principles of the invention, an exemplaryarticle having a photoactive surface, e.g., a photoactive coating, willfirst be described and then an exemplary method and kit fordemonstrating at least some of the photoactive properties of thesurface, e.g., photocatalytic activity and/or hydrophilicity (e.g.,photoactive hydrophilicity), in accordance with the invention will bedescribed. In the following discussion, the article will be referred toas an architectural window. However, it is to be understood that themethod and/or kit of the invention are not limited to use withphotoactive surfaces or architectural windows but can be practiced withany desired substrate, such as but not limited to tile substrates,ceramic substrates, and glass substrates and articles such as but notlimited to insulated glass units, and transparencies for air, sea-going,or land vehicles (such as automotive windshields, back lights,sidelights, moon roofs, etc.), just to name a few.

Referring to FIG. 1, there is shown a portion of an article 10 having asubstrate 12 with a first major surface 14 and a second major surface16. The substrate 12 is not limiting to the invention and may be of anydesired material having any desired characteristics, such as opaque,translucent, or transparent to visible light. By “transparent” is meanthaving a transmittance through the substrate of greater than 0% up to100%. By “visible light” or “visible region” is meant electromagneticenergy in the range of 395 nanometers (nm) to 800 nm. Alternatively, thesubstrate can be translucent or opaque. By “translucent” is meantallowing electromagnetic energy (e.g., visible light) to pass throughthe substrate but diffusing this energy such that objects on the side ofthe substrate opposite to the viewer are not clearly visible. By“opaque” is meant having a visible light transmittance of 0%. Examplesof suitable substrates include, but are not limited to, plasticsubstrates (such as acrylic polymers, such as polyacrylates,polyalkylmethacrylates, such as polymethylmethacrylates,polyethylmethacrylates, polypropylmethacrylates, and the like,polyurethanes, polycarbonates, and polyalkylterephthalates, such aspolyethyleneterephthalate (PET), polypropyleneterephthalates,polybutyleneterephthalates, and the like, or copolymers of any monomersfor preparing these, or any mixtures thereof); metal substrates; ceramicsubstrates; tile substrates; glass substrates; or mixtures orcombinations thereof. For example, the substrate can be conventionaluntinted soda-lime-silica-glass, i.e., “clear glass”, or can be tintedor otherwise colored glass, borosilicate glass, leaded glass, tempered,untempered, annealed, or heat-strengthened glass. The glass may be ofany type, such as conventional float glass or flat glass, and may be ofany composition having any optical properties, e.g., any value ofvisible transmission, ultraviolet transmission, infrared transmission,and/or total solar energy transmission. Types of glass suitable for thepractice of the invention are described, for example but not to beconsidered as limiting, in U.S. Pat. Nos. 4,746,347; 4,792,536;5,240,886; 5,385,872; and 5,393,593. Additionally, the glass can be acoated glass, such as SUNCLEAN® glass commercially available from PPGIndustries, Inc. of Pittsburgh, Pa. Other commercially available glasssuitable for use with the invention includes ACTIV® glass commerciallyavailable from Pilkington plc Corporation of Great Britain, or RADIANCE®glass or RADIANCE Ti™ glass commercially available from AFG Corporation,or BIOCLEAN™ glass or AQUACLEAN™ glass commercially available from St.Gobain, just to name a few.

In one non-limiting aspect of the invention, one or both of the surfaces14, 16 can have a photoactive coating 24, such as a photocatalytic orphotoactively hydrophilic coating. For example, the photoactive coating24 can be deposited over at least a portion of the substrate 12, e.g.,over all or a portion of the surface 14 and or the surface 16. In oneembodiment, the coating 24 can be photocatalytic, hydrophilic (e.g.,photoactively hydrophilic), or both. Although photoactive, the coating24 may not necessarily be photocatalytic to the extent that it isself-cleaning, i.e., may not be sufficiently photocatalytic to decomposeorganic materials like grime on the coating surface in a reasonable oreconomically useful period of time, but could still be hydrophilic.

The photoactive coating 24 material can include at least one metaloxide, such as but not limited to, one or more metal oxides orsemiconductor metal oxides, such as oxides of titanium, silicon (e.g.,silica), aluminum, iron, silver, cobalt, chromium, copper, tungsten,tin, vanadium, or zinc, or mixed oxides, such as zinc/tin oxides (e.g.,zinc stannate), strontium titanate and mixtures containing any one ormore of the above. The metal oxide can be crystalline or at leastpartially crystalline. In one exemplary coating 24, the photoactivecoating material can be all or at least partly titanium dioxide.Examples of suitable coatings 24 are found in (but are not limited to)U.S. Pat. applications Ser. Nos. 10/075,996 filed Feb. 14, 2002;60/305,191 filed Jul. 13, 2001; and 60/305,057 filed Jul. 13, 2001. Itis to be understood that the coating 24 is not limited to metal oxidesbut could include one or more nitrides, carbides, or mixtures orcombinations thereof, such as but not limited to one or more metalnitrides, metal carbides, metal oxides, or mixtures thereof. Otherexemplary coatings that can be utilized in the practice of the inventioninclude the coatings utilized on the commercially available coated glasssold under the trade names as mentioned above.

The coating 24 can be of any desired thickness and can be photocatalyticand/or hydrophilic (such as photoactively hydrophilic). As a generalrule, the thickness of the coating 24 to achieve photoactivehydrophilicity can be much less than is needed to achieve a commerciallyacceptable level of photocatalytic self-cleaning activity. For example,in one embodiment, the coating 24 can have a thickness in the range of10 Å to 5000 Å, where thicker coatings in this range can havephotocatalytic self-cleaning activity for at least some period of timeas well as hydrophilicity. As the coatings get thinner in this range,photocatalytic self-cleaning activity typically decreases in relation toperformance and/or duration. As coating thickness decreases in suchranges as 50 Å to 3000 Å, e.g., 100 Å to 1000 Å, e.g., 200 Å to 600 Å,e.g., 200 Å to 300 Å, photocatalytic self-cleaning activity may beunmeasurable but photoactive hydrophilicity can still be present in thepresence of selected electromagnetic radiation, e.g., activatingradiation within the photoabsorption band of the material.

The coating 24 can be deposited directly on, i.e., in surface contactwith, the surface 14 of the substrate 12 as shown in FIG. 1.Alternatively, one or more other layers or coatings can be interposedbetween the coating 24 and the substrate 12, such as but not limited toconventional alkali barrier layers or optical layers. For example, thecoating 24 can be an outer or the outermost layer of a multilayercoating stack or the coating 24 can be embedded as one of the layersother than the outermost layer within such a multilayer coating stack.By “an outer layer” is meant a layer receiving sufficient excitingelectromagnetic radiation, e.g., radiation within the photoabsorptionband of the layer material, to provide the coating 24 with sufficientphotoactivity to be at least photoactively hydrophilic if notnecessarily photocatalytic. In other non-limiting embodiments, thearticle 10 can be a piece of commercially available coated glass, suchas but not limited to those of the trade names mentioned above.

As discussed above, a problem in demonstrating many commerciallyavailable photoactive articles is that the photoactive surface orcoating typically has a photoabsorption band in the UV or visibleranges. Therefore, to demonstrate a photoactive article, such as awindow, to a potential customer, the photoactive surface needs to beexposed to ultraviolet and/or visible radiation within thephotoabsorption band of the material for a sufficient time before thedemonstration to render the surface photoactive. If not, the benefits ofthe photoactive surface, such as photocatalytic activity and/orhydrophilicity, cannot be adequately demonstrated to a customer.Oftentimes, salespeople simply place demonstration panels with aphotoactive surface in the trunk of their car or keep them inside anoffice building where the photoactive surface is not subjected tosufficient activating radiation to maintain the photoactive surface in aphotoactive state. Additionally, should a demonstration be scheduled fornighttime or for indoors, special lamps may be required to activate thephotoactive coating. Therefore, the invention provides a method ofdemonstrating and/or simulating and/or enhancing one or more photoactiveproperties of a photoactive surface, such as a UV and/or visiblephotoactive surface, in the absence of or at low levels of activatingradiation. By “low levels of activating radiation” is meant activatingradiation at a level such that the photoactive surface is not renderedphotoactive or is not rendered sufficiently photoactive to provide thesurface with demonstrable photoactive properties.

In one embodiment of the invention, a peroxide-containing material canbe deposited over or applied over at least a portion of the photoactivesurface. It has been found that the addition of a peroxide material toan inactive photoactive surface can provide the surface with properties,such as hydrophilicity, similar to that of the surface in a photoactivestate. In one embodiment, the photoactive surface can include titania,such as anatase and/or rutile and/or brookite titania and can includeone or more dopants such that the photoabsorption band includes one ormore wavelengths in the UV and/or visible ranges. In one embodiment, theperoxide material includes hydrogen peroxide. While the reason for thisresult is not completely understood at this time, it may be due to thehydrogen peroxide reacting with the titania to form Ti—OH sites on thesurface. These Ti—OH sites may provide the surface with properties, suchas hydrophilicity, simulating that of the surface in a photoactivestate.

In one embodiment, an aqueous solution of hydrogen peroxide can beapplied over the photoactive surface, e.g., over the coating 24. In oneembodiment, the hydrogen peroxide solution can contain between 1 wt. %to 30 wt. % hydrogen peroxide, such as 3 wt. % to 7 wt. %, such as 3 wt.%. The hydrogen peroxide solution can be applied in any conventionalmanner, such as by spraying or wiping. The hydrogen peroxide solutioncan be allowed to dry on the surface before demonstrating thephotoactivity simulating properties of the surface, such ashydrophilicity. For example, the hydrogen peroxide solution can be driedat ambient temperatures, typically in the range of 50° F. to 90° F. (10°C. to 32° C.) for a time sufficient to vaporize the aqueous solution.Alternatively, the applied aqueous hydrogen peroxide solution can bedried at ambient temperatures for a period in the range of 3 minutes to60 minutes, such as 5 minutes to 40 minutes, such as 10 minutes. Afterwhich, the hydrophilicity of the surface can be demonstrated by sprayingor applying distilled or deionized water onto the surface. It isbelieved that photocatalytic activity may be demonstrated by applying anorganic material onto the surface and, optionally, exposing the surfaceto electromagnetic radiation having one or more wavelengths in the UVand/or visible regions.

A demonstration kit 30 in accordance with the invention is shown in FIG.2. The demonstration kit 30 can include a sample substrate 32 with atleast a portion 34 of the substrate having a photoactive surface, suchas a photoactive coating (e.g., a UV and/or visible photoactivecoating), deposited thereon. Another portion 36 of the substrate 32 canbe free of photoactive coating and can be present to provide acomparison between the photoactive surface and the non-photoactivesurface. The kit 30 can also include a stand 38 to hold the substrate 32during a demonstration. In a further embodiment, the kit 30 can includea container 40, such as a plastic squeeze bottle, containing an aqueoussolution of a peroxide material. In one embodiment, the container 40includes a 3 wt. % to 7 wt. % aqueous solution of hydrogen peroxide. Thekit 30 can further include one or more applicators 42 to apply theperoxide material onto the surface. The applicator 42 can be anymaterial or device to apply the peroxide material, such as but notlimited to one or more rigid or foam applicators, sponges, and/or one ormore absorbent pads 44 Optionally, the kit 30 can further include acontainer 46, such as a plastic squeeze bottle, containing water to beused to demonstrate the hydrophilicity of the surface. Optionally, thekit can further include a glass cleaning solution, such as Windex® brandwindow cleaner commercially available from SC Johnson. The variouselements of the kit 30 can be provided in a carrying case, a bag, orsimilar device.

While the above demonstration method works well, it has been found thatafter the hydrogen peroxide solution is applied to the photoactivesurface 34 and the surface 34 has been sprayed with water about 4 or 5times to demonstrate the hydrophilicity of the surface, the contactangle of water on the surface begins to rise. This may be due to theaccumulation of contaminants on the surface 34. Therefore, in a furtherembodiment of the invention and as shown in FIG. 1, a thin layer of aresinous material 50 can be applied over the photoactive coating 24 toincrease the number of times the substrate (e.g., the photoactiveportion 34) can be sprayed with water to demonstrate hydrophilicitybefore having to again refresh the surface with hydrogen peroxide. By“refresh the surface” is meant reapplying peroxide material until thesurface again displays hydrophilicity. In one embodiment, the resinousmaterial 50 can include a siloxane material, such as an at least partlyhydrolyzed siloxane material such as an at least partly hydrolyzedpolyalkoxysiloxane material. By “at least partly hydrolyzed” is meantthat at least a portion of the alkoxy groups (e.g., —OCH₃ groups) arereplaced with (—OH) groups. For example, the polyalkoxysiloxane can begreater than 50% hydrolyzed, such as greater than 60% hydrolyzed, suchas greater than 70% hydrolyzed, such as in the range of 80% to 100%hydrolyzed. Examples of suitable hydrolyzed or partly hydrolyzedpolyalkoxysiloxane materials include, but are not limited to, at leastpartly hydrolyzed polymethoxysiloxane, polyethoxysiloxane,polypropoxysiloxane, and/or polybutoxysiloxane. The siloxane materialcan be provided in an aqueous solution and can be applied onto thephotoactive surface in any conventional manner, such as by spraying orwiping. One example of a suitable siloxane material is MKC SilicatesMS-1200® (hereinafter “MS-1200®”) commercially available from MitsubishiChemical America, Inc. of White Plains, N.Y. MS-1200® is comprised ofthe reaction products of the acid catalysis of tetramethylorthosilicateto partially hydrolyzed polymethoxysiloxane in a solution of water,methanol, and ethanol. The at least partly hydrolyzed siloxane materialcan be applied over the photoactive surface 34 and then dried in anyconventional manner, such as by air drying at ambient temperatures for atime sufficient to dry the applied siloxane material. In one embodiment,the siloxane material can be dried at ambient temperatures for a periodof one minute to greater than or equal to 2 hours. Alternatively, thesiloxane material can be dried at ambient temperatures for a period of 1minute to 60 minutes, such as 5 minutes to 60 minutes, such as 20minutes to 40 minutes, such as 30 minutes and then optionally heated toa temperature of about 40° C. to 100° C., such as 45° C. to 80° C., suchas 45° C. to 60° C., such as 50° C. for about one minute to 60 minutes,such as 5 minutes to 60 minutes, such as 20 minutes to 40 minutes, suchas 30 minutes to dry the siloxane material, remove the solvent and/oracid, and promote good bonding to the surface. The siloxane material canbe applied to any thickness so as not to adversely impact upon thephotoactive characteristics, such as photocatalysis and/orhydrophilicity (e.g., photohydrophilicity) of the underlying photoactivecoating. In one embodiment, the siloxane material can be applied toprovide a siloxane layer having a thickness of less than or equal to 10nm, such as less than or equal to 5 nm, such as less than or equal to 4nm, such as less than or equal to 3 nm, such as in the range of 2 nm to3 nm.

After the siloxane material has been applied over the photoactivesurface, a peroxide material, such as an aqueous hydrogen peroxidesolution as described above, can be applied over the siloxane coating.The resultant article has been found to exhibit or simulate photoactivecharacteristics, such as hydrophilicity, when exposed to electromagneticradiation having one or more wavelengths in the visible region.Additionally, the siloxane material at estimated thickness of less thanor equal to 5 nm has been demonstrated not to adversely impact upon thephotocatalytic activity of the underlying photoactive coating (see FIG.3).

In this aspect of the invention, the kit 30 shown in FIG. 2 can furtherinclude a container 54 containing a siloxane material, such as an atleast partially hydrolyzed polyalkoxysiloxane solution (e.g., apartially hydrolyzed polymethoxysiloxane, polyethoxysiloxane, orpolypropoxysiloxane, solution, or mixtures thereof), as described above.This polyalkoxysiloxane solution can be applied to the surface of thesubstrate as described above before demonstrating the substrate to apotential customer. In one embodiment, the at least partly hydrolyzedpolymethoxysiloxane material comprises less than 1 weight percentMS-1200®, such as less than 0.8 weight percent MS-1200®, such as lessthan 0.5 weight percent MS-1200®, such as 0.1 weight percent MS-1200® inwater.

In the exemplary embodiments discussed above, the peroxide materialand/or the at least partially hydrolyzed siloxane material weredeposited over a substrate having a photoactive coating. However, inanother aspect of the invention, the peroxide material and/or thesiloxane material can be deposited over a non-photoactive substrate,such as a piece of clear glass, to simulate the hydrophilic effect of anactivated photoactive surface. For example, the siloxane material can bedeposited directly onto a piece of clear glass and allowed to dry. Thecoated glass can then be contacted with water. It has been found thatthe water, if it has a contact angle of less than about 20°, appears towet-out the surface and can be used to demonstrate what the property ofphotoactive hydrophilicity will appear like with an activatedphotoactive surface.

In another aspect of the invention, a peroxide solution, such asdescribed above, can be used to clean an installed window having aphotoactive surface to provide immediate hydrophilicity even in theabsence of photoactive activity. For example, if an installed windowhaving a photoactive surface (e.g., a titania-containing surface) ceasesto demonstrate photoactive properties, such as hydrophilicity, due tothe accumulation of contaminants, the surface can be cleaned with aperoxide solution such as described above to remove the contaminants.The peroxide material can interact with the surface, such as to formTi—OH sites as described above, to provide hydrophilicity at least forpart of the time while the photoactive surface becomes active again.

The general concepts of the invention will be further described withreference to the following examples. However, it is to be understoodthat the following examples are merely illustrative of the generalconcepts of the invention and are not intended to be limiting.

EXAMPLE 1

This example illustrates a method to demonstrate or simulate hydrophilicproperties of a photoactive surface utilizing hydrogen peroxide when thephotoactive surface is inactive or is exposed to electromagneticradiation in the visible region.

Two 4 inch by 4 inch (10 cm by 10 cm) SUNCLEAN® coated glass substrates(samples 1 and 2) and two 4 inch by 4 inch (10 cm by 10 cm) substratesof clear float glass (samples 3 and 4) obtained from PPG Industries,Inc. of Pittsburgh Pa. The SUNCLEAN® glass substrates were exposed to UVradiation for a sufficient time to render the substrates photoactive.The clear float glass substrates were polished with a slurry of cesiumoxide. The contact angle of a water drop was then measured on both thepolished float glass and SUNCLEAN® surfaces. For each substrate, fivecontact angle measurements were made and the results are shown in Table1 below. As can be seen, the activated SUNCLEAN® glass had lower contactangle measurements than the polished float glass.

TABLE 1 Contact Angle Measurements Sample 1 2 3 4 5 Average 1  2° 3°  2° 8° 4° 4° 2  5° 2° 15°  5° 7° 7° 3 10° 6° 10° 11° 9° 9° 4 16° 10°   9°10° 10°  10° 

Next, the substrates were placed in a laboratory (without access tosolar radiation) for a period of about 12 hours to deactivate ordecrease the hydrophilicity of the SUNCLEAN® glass. The contact anglemeasurements were repeated and the results of these measurements areshown in Table 2 below. As shown in Table 2, the deactivated SUNCLEAN®glass had higher contact angle measurements than the activated SUNCLEAN®glass reported in Table 1.

TABLE 2 Contact Angle Measurements Sample 1 2 3 4 5 Average 1 30° 31°30° 44° 34° 34° 2 44° 58° 44° 38° 40° 45° 3 20° 25° 23° 20° 21° 22° 423° 20° 20° 19° 20° 20°

Next, a 3 wt. % aqueous hydrogen peroxide solution (commerciallyavailable from the Cumberland Swan Company) was applied to thedeactivated SUNCLEAN® glass substrates and clear glass substrates. Theperoxide solution was poured onto the substrate surfaces and then wipedwith a BloodBloc pad (commercially available from Fisher Scientific).The aqueous peroxide solution was applied until the surfaces achievedwet-out. By “wet-out” is meant that a substantially uniform layer of theperoxide solution was formed over the surface without pooling, beading,or pull-back along the edges. The peroxide liquid was dried at ambienttemperature for about 3 to 5 minutes and then contact angle measurementswere again taken on the substrates in the laboratory (i.e., in theabsence of direct solar radiation). The results of these contact anglemeasurements are shown in Table 3 below.

TABLE 3 Contact Angle Measurements Sample 1 2 3 4 5 Average 1  8°  6°11° 10°  8°  9° 2 15°  9° 11° 13° 16° 11° 3 25° 25° 24° 27° 23° 25° 428° 30° 28° 30° 23° 28°

As shown in Table 3, the deactivated SUNCLEAN® glass substrates with thehydrogen peroxide solution displayed much lower contact angle resultsthan for the clear glass substrates. However, it should be noted thatthe hydrogen peroxide coated deactivated SUNCLEAN® glass still hadhigher contact angle results than the photoactivated SUNCLEAN® glasssamples of Table 1.

EXAMPLE 2

This example illustrates the use of a thin, durable resinous coatingapplied over a substrate to simulate the hydrophilicity of an activatedsubstrate even in the absence of solar radiation. The presence of theresinous coating does not appear to adversely impact upon thephotoactivity of an underlying photoactive coating, if present, and thepresence of the resinous coating appears to maintain the hydrophilicityof the article for more subsequent water washes than the direct hydrogenperoxide application method described in Example 1.

Samples of SUNCLEAN® glass substrates were obtained from PPG Industries,Inc. of Pittsburgh, Pa. In the following experiment, the SUNCLEAN® glasswas in a deactivated state. Two of the samples (samples 5 and 6) wereused as controls. Three of the samples (samples 7, 8, and 9) were coatedwith a resinous coating in the following manner. The substrates werecleaned on both sides using a diluted Dart-210 cleaning solution(commercially available from Madison Chemical Company, Inc.) and thenrinsed with distilled water. The substrates were laid (coating side up)on a clean, lint-free surface and wiped with TechniCloth® wipes(commercially available from Texwipe Company, llc). The substrates werethen cleaned with Windex® brand window cleaner (commercially availablefrom SC Johnson) and wiped with a Kaydry wipe (commercially availablefrom Kimberly Clark Company). A 4 inch by 4 inch (10 cm by 10 cm)BloodBloc pad (commercially available from Fisher Scientific) waswrapped around a foam applicator with the fiber side out. Approximately1.5 ml of 3 wt. % hydrogen peroxide solution was placed on the pad andapplied onto the substrate by wiping the pad over the substrate usingoverlapping strokes. The hydrogen peroxide solution was applied untilthe solution wet-out the substrate. The hydrogen peroxide solution wasthen air dried at ambient temperature (about 70° F. (21° C.) for about 3minutes to 10 minutes.

To form the resinous coating, a 0.1 wt. % solids aqueous solution ofMS-1200® was prepared by commercially purchasing a 1 wt. % container ofMS-1200® and diluting the commercially available liquid with a mixtureof 50 volume percent distilled water and 50 volume percent 2-propanol toform a 0.1 wt. % aqueous solution of MS-1200®. A fresh BloodBloc pad waswrapped around the foam applicator with the fiber side out andapproximately 1.5 ml of the 0.1 wt. % MS-1200® solution was applied tothe pad. The pad was wiped across the glass surface using overlappingstrokes until the glass was coated. The applied MS-1200® coating wasallowed to air dry at ambient temperature for between 5 minutes to 30minutes. The substrates were then placed in an oven and heated to 50° C.for 30 minutes. After which, the glass substrates were removed from theoven and allowed to cool to ambient conditions.

A third set of samples (samples 10, 11, and 12) was prepared in similarmanner as described above for samples 7-9 but were allowed to cure underthe exposure of UVA-340 irradiation at 28W/m^(2.)

Additionally, samples 5-12 were tested for photocatalytic activity byusing a conventional stearic acid test. A detailed description of thestearic acid test is disclosed, for example, in U.S. Pat. No. 6,027,766,herein incorporated by reference. The results of these tests are shownin FIG. 3.

The results of these tests are shown in FIG. 3. When absorbance of the—CH₂ stretching band from 2965 cm ⁻¹ to 2820 cm ⁻¹ of the stearic acidis followed as a function of UVA-340 exposure, the rate of decompositionis proportional to the slope of the linear fit. These results (shown inTable 4 below) indicate that the MS-1200® coating did not significantlyhinder or accelerate the rate of photocatalytic decomposition of thestearic acid.

TABLE 4 Linear Regression Photoactivity Fit (−m × 1000) y = mx + b R²cm⁻¹/min Sample 5 y = −0.009x + 0.541 0.995 9 Sample 6 y = −0.008x +0.487 0.996 8 Sample 7 y = −0.009x + 0.424 0.995 9 Sample 8 y =−0.008x + 0.427 0.995 8 Sample 9 y = −0.008x + 0.415 0.994 8 Sample 10 y= −0.010x + 0.419 0.998 10 Sample 11 y = −0.010x + 0.404 0.997 10 Sample12 y = −0.009x + 0.415 0.993 9

EXAMPLE 3

This example illustrates that a hydrophilic surface can be obtained on adeactivated photoactive coating without direct solar electromagneticradiation.

A 10 inch by 9 inch (25 cm by 23 cm) piece of SUNCLEAN® coated glass wasobtained from PPG Industries, Inc. and kept in a laboratory withoutaccess to solar radiation for 2 days to ensure the glass was notphotoactive. The contact angle of a water droplet on this glass wasmeasured to be 47°. The glass was then placed in a dark room (withoutexposure to visible or UV radiation) and a 3 wt. % hydrogen peroxideaqueous solution was applied over the coated glass as described inExample 1. Infrared light was used during this experiment so that theglass was not exposed to either UV or visible light. After applicationof the hydrogen peroxide solution, the contact angle of the waterdroplet was measured to be 8°. Thus, the hydrophilic surface provided bythe application of hydrogen peroxide onto a titania-containing coatingwould appear to be formed even in the absence of both UV and visiblelight.

EXAMPLE 4

This example demonstrates the effect of hydrogen peroxide treatment witha photoactive substrate having different concentrations of MS-1200®under two different curing methods.

4 inch by 4 inch (10 cm by 10 cm) samples of SUNCLEAN® coated glass(commercially available from PPG Industries, Inc.) were obtained and anaqueous layer of MS-1200 ® was applied to the substrates as describedabove in Example 2 but at different wt. % concentrations of MS-1200® asshown in Table 5. After application of the MS-1200®, the substrates weredried (e.g., cured) in two different manners. In one method, thesubstrates were heated to a temperature of 50° C. for 30 minutes to drythe MS-1200® liquid. In the second method, the MS-1200® coatedsubstrates were simply allowed to air dry at ambient temperature for aperiod of about 12 hours.

Table 5 below shows the contact angle results for a water droplet on thecoated substrates before and after 3 wt. % hydrogen peroxide applicationwith different concentrations of MS-1200® under different curingconditions.

TABLE 5 Contact Angles % solids 50° C. cure Ambient overnight cureMS-1200 ® before after before after 0.1 26°  9° 26° 10° 0.15 25° 10° 22° 9° 0.2 23° 10° 22° 10° 1 23°  9° 27°  9°

EXAMPLE 5

A 6 inch by 12 inch (15 cm by 30 cm) piece of SUNCLEAN® coated glass wascoated with a 0.2 wt. % MS-1200® liquid as described above in Example 2.The coated glass was exposed to sunlight outdoors for 2 hours and thecontact angle of a water droplet on the coated glass surface wasmeasured to be 4°. This suggests that 0.2 wt. % of the MS-1200® coatingwill not adversely affect the hydrophilicity and photoactivity of thetitania coating.

It will be readily appreciated by those skilled in the art thatmodifications may be made to the invention without departing from theconcepts disclosed in the foregoing description. Accordingly, theparticular embodiments described in detail herein are illustrative onlyand are not limiting to the scope of the invention, which is to be giventhe full breadth of the appended claims and any and all equivalentsthereof.

1. A kit for demonstrating hydrophilicity of a surface, comprising: a substrate having a surface, with a photoactive coating provided over at least a portion of the surface; a container comprising an aqueous peroxide material; and a container comprising an at least partly hydrolyzed siloxane material.
 2. The kit of claim 1, wherein the substrate surface has a first portion having the photoactive coating and a second portion free of the photoactive coating.
 3. The kit of claim 1, wherein the photoactive coating includes at least one metal oxide.
 4. The kit of claim 3, wherein the at least one metal oxide is selected from the group consisting of one or more oxides of titanium, silicon, aluminum, iron, silver, cobalt, chromium, copper, tungsten, tin, vanadium, zinc, and mixtures thereof.
 5. The kit of claim 3, wherein the at least one metal oxide is at least partly crystalline.
 6. The kit of claim 3, wherein the at least one metal oxide comprises titanium dioxide.
 7. The kit of claim 1, wherein the peroxide material comprises hydrogen peroxide.
 8. The kit of claim 1, wherein the at least partly hydrolyzed siloxane material comprises an aqueous solution comprising at least one at least partly hydrolyzed polyalkoxysiloxane material.
 9. The kit of claim 8, wherein the solution comprises from 0.1 wt. % to 5 wt. % of at least partly hydrolyzed polymethoxysiloxane.
 10. A kit for demonstrating hydrophilicity of a surface, comprising: a substrate having a surface, with a photoactive coating provided over at least a portion of the surface, wherein the photoactive coating includes at least one metal oxide selected from the group consisting of one or more oxides of titanium, silicon, aluminum, iron, silver, cobalt, chromium, copper, tungsten, tin, vanadium, zinc, and mixtures thereof; a container comprising an aqueous peroxide material, wherein the peroxide material comprises hydrogen peroxide; and a container comprising an at least partly hydrolyzed siloxane material, wherein the at least partly hydrolyzed siloxane material comprises an aqueous solution comprising at least one at least partly hydrolyzed polyalkoxysiloxane material.
 11. The kit of claim 10, wherein the siloxane material comprises from 0.1 wt. % to 5 wt. % of at least partly hydrolyzed polymethoxysiloxane.
 12. A kit for demonstrating hydrophilicity of a surface, comprising: a substrate having a surface, with a photoactive coating provided over a first portion of the surface and with a second portion of the surface being free of the photoactive coating, wherein the photoactive coating comprises titanium dioxide; a container comprising an aqueous peroxide material comprising hydrogen peroxide; and a container comprising an aqueous solution comprising 0.1 wt. % to 5 wt. % of at least partly hydrolyzed polymethoxysiloxane. 